Originally Posted by
husaberg
yes i realise an MMC material would be probably better but does anyone have any ideas?
No.
Other than to suggest the 7000 series cast tooling grade alloys are most stable both mechanicaly and thermally.
Guess annodising would add wear resistance, but it's not very thick. Wonder if the ceramic coating used on zorsts would stay bonded to alloy.
With enough cash you could play with explosive clad composites like toolsteel/alloy/toolsteel. Even then I'd think you'd have trouble keeping them bonded.
PS: if you've got plenty of cash let me know.
PPS: Have talked to NZ cylinders about chrome alloy disks?
Go soothingly on the grease mud, as there lurks the skid demon